E501T-1, E71T-1
Use is CO2 flux cored wire for welding titanium. High deposition efficiency, excellent all-position welding performance can also be vertical down welding. For ships, pressure vessels, mechanical equipment, steel bridges, steel low carbon steel and 490MPa grade high strength steel welding. Standard:
GB / T: E501T-1
AWS: E71T-1
| Package |
Package |
Silk panel |
Net weight |
| Φ1.0~1.6(mm) |
D100mm D200mm D270mm D300mm K300mm |
1 kg, 5 kg, 15 kg18 kg, 20 kg |
| Chemical (%) |
C |
Mn |
Si |
P |
S |
|
| ≤0.10 |
≤1.75 |
≤0.75 |
≤0.03 |
≤0.03 |
|
| Deposited metal Mechanical properties |
Yield strengthσ0.2(Mpa) |
Tensile strengthσb(Mpa) |
Elongationδ5(%) |
AKV Impact Energy(J) |
| ≥400 |
≥480 |
≥22 |
≥47(0℃) |
≥47(-20℃)
|
| Wire diameter(mm) |
Φ1.0 |
φ1.2 |
φ1.4 |
φ1.6 |
Welding position |
|
| Welding current(AMP.) |
80~250 |
120~300 |
160~400 |
190~450 |
| Notes: |
1 wire into the plant must be stored in a dry environment, not just open the disk waterproof wire welding package 2 should be removed before welding surface of the oil, rust, moisture and other impurities
3. The use of CO2 gas, CO2 gas purity of 99.98%.
4 CO2 protection welding gas flow should be controlled in 20-25L/min.
5 out of wire length should be controlled at 15-25mm range.
6 to be preheated before welding to 150-300 ℃, after welding to be tempered by 700-740 ℃. |
We support OEM production, so we can purchase materials according to your needs to achieve more suitable prices.
We have a very strict test system, and the product yield is 95%. GB50-6 is our QC standard.
We use a layered design for barreled welding wire to ensure better use and preservation of the product.